Effect of the new hydrogels loaded with plateletrich fibrin on chondrogenic differentiation of BMSCs
CHEN Xing-guang1,2, ZOU Cheng-da1,2, SU Guang-hao1, ZHANG Ya1, LU Min-hua3, WANG Xiao-dong2
（1. Pediatrics Research Institute， 2. Department of Orthopaedics, Children′s Hospital of Soochow University, Suzhou Jiangsu 215025; 3. Department of Orthopaedics, Suzhou Dushuhu Public Hospital, Suzhou Jiangsu 215025, China）
Abstract：Objective: To explore effect of the new hydrogels loaded with plateletrich fibrin(PRF) on chondrogenic differentiation of BMSCs. Methods: 2% chitosan (CS) solution, 56% βglycerophosphate (βGP) solution and 0.1% genipin solution were mixed with the ratio of 6 ∶1 ∶1 to get the CS/GP/0.1% genipin mixed solution, and measured its gelformation time at 37 ℃.Then PRF was prepared by once centrifugation (1 200 r/min, 12 min), and the freezedrying PRF was ground into powder, which was added into that mixed solution. New type hydrogels were made with PRF at 37 ℃. The BMSCs were seeded on the surface of the hydrogels, and the state of cell growth was observed by FDA fluorescent staining. For chondrogenic induction, BMSCs were then cultured in the 24well plate, by adding the new type of hydrogels, chitosan thermosensitive hydrogels or empty control at the same time. Effect of the new type of hydrogels on chondrogenic differentiation were observed by HE staining, safranin Ofast green staining, alcian blue staining and immunohistochemical staining of type Ⅱ collagen 2 weeks after cell culture. The amount of glycosaminoglycans (GAGs) in the supernatant was quantitatively determind by alcian blue colorimetric assay 4 weeks after cell culture. The amount of type Ⅱ collagen in supernatant was quantitated by ELISA 4 weeks after cell culture. Results: The gelformation time of the volume ratio of 6 ∶1 ∶1 of the CS/GP/0.1% genipin mixed solution was about 8 min at 37℃. The BMSCs seeded on the surface of the hydrogels presented good proliferation. For the group of the new type of hydrogels, the result of HE staining, safranin Ofast green staining, alcian blue staining and immunohistochemical staining of type Ⅱ collagen were positive, and the other two group were weakly positive. There are GAGs and type Ⅱ collagen in the supernatant of three groups. But there are statistical significance between the group of the new type of hydrogel and the other groups for the difference in secretion of GAGs and type Ⅱ collagen (P<0.05). Conclusion: That hydrogel have a good biocompatibility with BMSCs, and the BMSCs seeded on the surface of the hydrogels presented good proliferation. The new type hydrogels with PRF were able to promote chondrogenic differentiation to a certain degree.
陈星光1，2， 邹承达1，2， 宿广昊1， 张亚1， 陆敏华3， 王晓东2. 负载富血小板纤维蛋白的新型水凝胶对BMSCs体外成软骨分化的影响[J]. 江苏大学学报:医学版, 2018, 28(04): 291-296.
CHEN Xing-guang1,2, ZOU Cheng-da1,2, SU Guang-hao1, ZHANG Ya1, LU Min-hua3, WANG Xiao-dong2. Effect of the new hydrogels loaded with plateletrich fibrin on chondrogenic differentiation of BMSCs. Journal of Jiangsu University(Medicine Edition), 2018, 28(04): 291-296.
［1］杨泽龙. 利用胶原—透明质酸—硫酸软骨素三元纳米支架修复兔关节软骨缺损的实验研究\[D\]. 泸州：泸州医学院, 2014.［2］Verdonk P, Dhollander A, Almqvist KF, et al. Treatment of osteochondral lesions in the knee using a cellfree scaffold\[J\]. Bone Joint J,2015,97B(3):318-323.［3］Chenite A, Chaput C, Wang D, et al. Novel injectable neutral solutions of chitosan form biodegradable gels in situ\[J\]. Biomaterials,2000,21:2155-2161.［4］Zhou HY, Jiang LJ, Cao PP, et al. Glycerophosphatebased chitosan thermosensitive hydrogels and their biomedical applications\[J\]. Carbohydr Polym, 2015,117:524-536.［5］Choukroun J, Diss A, Simonpieri A, et al. Plateletrich fibrin (PRF): a second generation platelet concentrate. Part Ⅴ: histologic evaluations of PRF effects on bone allograft maturation in sinus lift\[J\]. Oral Surg Oral Med Oral Pathol Oral Radiol Endod，2006,101(3)：299-303.［6］Honda H, Tamai N, Naka N, et al. Bone tissue engineering with bone marrowderived stromal cells integrated with concentrated growth factor in Rattus norvegicus, calvaria defect model\[J\]. J Artif Organs, 2013, 16(3):305-315.［7］陈星光. 负载PRF的新型水凝胶对骨髓间充质干细胞体外成软骨分化影响的研究\[D\]. 苏州：苏州大学, 2018.［8］中国疾病预防控制中心. 实验动物相关法规标准汇编 2009年版\[M\]. 北京: 北京大学医学出版社，2009.［9］冯笑, 韩絮, 张亚,等. 与软骨细胞共培养促进BMSCs分化为软骨细胞\[J\]. 江苏大学学报(医学版), 2017, 27(5):403-407.［10］秦汉, 王剑,杨涛, 等. 石墨烯/壳聚糖,β甘油磷酸钠温敏凝胶的制备及其性能评价\[J\]. 口腔颌面修复学杂志,2016,17(5):257-262.［11］于斐, 曾晖, 于红燕, 等. 软骨细胞特殊染色技术的比较与应用\[J\]. 中国比较医学杂志, 2015, 25(8):58-61.［12］胡志俊, 胡波, 唐德志, 等. 兔膝关节软骨细胞的分离培养及形态学特征\[J\]. 中国组织工程研究与临床康复, 2010(46):8555-8558.［13］任晓春. 体外软骨细胞与软骨单位共培养构建软骨组织工程种子细胞的最佳比值\[D\]. 太原：山西医科大学, 2013.［14］胡斌. 骨髓间充质干细胞与软骨细胞聚集共培养修复兔膝关节骨软骨缺损的研究\[D\]. 苏州：苏州大学, 2016.［15］Bhattacharjee M, Coburn J, Centola M, et al. Tissue engineering strategies to study cartilage development, degeneration and regeneration\[J\]. Adv Drug Deliv Rev,2015,84:107-122.［16］郭晓东, 杜靖远, 郑启新,等. 转化生长因子β1基因修饰的间充质干细胞/仿生基质材料的体外复合培养\[J\]. 中国医学科学院学报, 2001, 23(4):373-377.［17］宗传晖, 徐国园, 孙熠昂,等. 壳聚糖接枝共聚改性最新研究进展\[J\]. 高分子通报, 2017(5):19-28.［18］曹峥, 胡蕴玉, 潘纬敏,等. 交联温度对京尼平交联胶原/壳聚糖组织工程支架的影响\[J\]. 中国矫形外科杂志, 2009, 17(3):217-220.［19］Sung HW, Chang Y, Chiu CT, et al. Mechanical properties of a porcine aortic valve fixed with a naturally occurring crosslinking agent\[J\]. Biomaterials, 1999, 20(19):1759.［20］付勤, 王勇, 于冬冬, 等.外源性TGFβ1及IGF1诱导大鼠脂肪干细胞向软骨细胞分化的实验研究\[J\].中国骨质疏松杂志,2007,13(12):848-853.
2018, Vol. 28 