Cause analysis for large titanium inclusion in wire rod cord steel
Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan, Hubei 430081, China
Abstract:To simulate the dissolution behavior of foreign titanium inclusion particle in molten steel, the tire cord steel casting slabs from production field were remelted through vacuum induction furnace in the laboratory, and the artificially prepared TiN particles with size of 50~74 μm and 100~180 μm were added during remelting process. Combined with the dissolution kinetic model of TiN particle,the genesis of lagre titanium inclusion in wire rod was analyzed. The dissolution dynamics calculation of TiN particle show that the TiN particle with size of 180 μm dissolves in liquid steel completely only for a few seconds. The titanium inclusions in the remelted specimens are regular shape, which mainly come from the precipitations in liquid steel during solidification process rather than the adding residual of uncompletely dissolved TiN particle. It is supposed that the large titanium inclusion in wire rod most likely comes from continuous casting mould fluxes.
雷家柳, 薛正良. 帘线钢盘条中大颗粒钛夹杂成因分析[J]. 江苏大学学报(自然科学版), 2016, 37(6): 670-674.
LEI Jia-Liu, XUE Zheng-Liang. Cause analysis for large titanium inclusion in wire rod cord steel[J]. Journal of Jiangsu University(Natural Science Eidtion)
, 2016, 37(6): 670-674.