| Effect of middle layer by liquidphase deposition technology on bonding strength of porcelain and pure titanium |
| JIANG Tao1, CHEN Wei-jun2, FENG Ge1, XUAN Zhi-gang1, WU Zhanao1, GAO Yu1 |
| （1.Department of Stomatology, the 359 Hospital of PLA, Zhenjiang Jiangsu 212001; 2.Medical Department,Hospital of PLA 73056 Unit, Zhenjiang Jiangsu 212004, China） |
|
|
|
|
Abstract [Abstract]Objective: To investigate the effect of middle layer with liquidphase deposition（LPD） technology on bonding strength of titanium and porcelain in different condition. Methods： Fifty pure titanium specimens were randomly divided into ten groups（n=5）according to different surface treatments after sandblasting. The surface of titanium was investigated by scanning electron microscope(SEM）.After the middle area of the samples was veneered with porcelain, a threepointflexuretest was used to evaluate the bonding strength of titanium to porcelain.Results： The bonding strength of groups of liquidphase deposition were significantly higher than control group(P＜0.05). The mean bonding strength of pH=9,0.3 mol/L silicate solution group was the highest\[(38.86±2.63)MPa\], it was significantly higher than those of other nine groups(P＜0.05). Conclusion： Middle layer prepared by LPD technology was significant in improving bonding strength of porcelain and pure titanium, the bonding strength was the highest by pH=9,0.3 mol/L silicate solution.
|
|
Received: 09 June 2013
|
|
|
|
| [1]Starosvetsky D, Gotman I. Corrosion behavior of titanium nitride coated Ni-Ti shape memory surgical alloy[J].Biomaterials,2001,22(13):1853-1859. [2]高宇,吴占敖,殷恒波,等.液相沉积中间层对2种钛瓷粉的钛瓷结合强度的影响[J].口腔医学研究,2013,29(4：)319-322.[3]International Organization for Standardization. ISO 9693（1999）Amd.1 2005(E). Metalceramic dental restorative systems[S]. ISO/TC, 2005.[4]Kononen M，Kivilahti J.Bonding of low-fusing dental porcelain to commercially pure titanium[J].J Biomed Mater Res，1994，28(5):1027-1035.[5]吕武龙,张振庭,任卫红,等.不同厚度溶胶凝胶法二氧化硅薄膜对钛瓷结合强度的影响[J].口腔颌面修复学杂志,2010,11(3):135-137.[6]李健学,姚宏,田文艳,等.不同处理方法对钛瓷结合强度影响的研究[J].现代生物医学进展, 2012,12(11):2027-2030.[7]周淑,王瑜,章非敏,等.纳米硅涂层对钛瓷结合强度的影响[J].华西口腔医学杂志,2009, 27（3）:276-279.[8]Bienias＇ J, Surowska B, Stoch A,et al. The influence of SiO2 and SiO2-TiO2 intermediate coatings on bond strength of titanium and Ti6Al4V alloy to dental porcelain[J]. Dent Mater,2009,25(9):1128-1135.[9]Nagayama H,Honda H,Kawahare H.A new process for silica coating[J].J Electrochem Soc,1988,135(8):2013-2016.[10]狄平,朱世根,顾伟生.合金元素Si在钛合金中作用的研究进展[J].金属热处理,2007,32(11):5-10.[11]黄选民,侯廷红,幸泽宽.氮化钛涂层及其复合涂层的研究进展[J].电镀与精饰, 2009,31(2):12-15.[12]Kelly M, Asgar K,OBrien WJ. Tensile strength determination of the interface between porcelain fused to gold[J].J Biomed Mater Res,1969,3(3):403-408. |
|
|
|
2013, Vol. 23 