Abstract：A monolithic catalyst Pt/support/cordierite was prepared with hydrogen zeolite sieve molecular-5 (HZSM-5) and oxides (Al2O3，TiO2 and SiO2) coating as support, cordierite as matrix and Pt as active component. The structure and properties of the catalyst were characterized by XRD, SEM, TEM and XPS. The effects of carriers and Pt loads on the catalytic reaction performance of hydrogen in low temperature were investigated when the volume concentration of hydrogen is 2.5%. The results show that the monolithic catalyst supported by HZSM-5 has the best performance, which is related to the good adhesion of the active layer, the good distribution of Pt and the uniform particle size. The catalyst with SiO2 as support shows the worst performance, because the support has the least Pt0 with weak Pt load. Pt/HZSM-5/cordierite monolithic catalyst shows better catalytic activity when the load of Pt is 0.01 g·L-1. With Pt load of 0.05 g·L-1 and more, Pt/HZSM-5/cordierite monolithic catalyst can rapidly set up even at room temperature and achieve 100% conversion.
周颖， 唐爱坤， 倪强， 李冲. 不同载体Pt基整体式催化剂对氢气低温反应性能的影响[J]. 江苏大学学报（自然科学版）, 2023, 44(2): 207-212.
ZHOU Ying, TANG Aikun, NI Qiang, LI Chong. Effect of Pt-based monolithic catalysts with different support on low temperature reaction performance of hydrogen[J]. Journal of Jiangsu University(Natural Science Eidtion)
, 2023, 44(2): 207-212.
DARIF B, OJALA S, PIRAULT-ROY L, et al. Study on the catalytic oxidation of DMDS over Pt-Cu catalysts supported on Al2O3, AlSi20 and SiO2[J]. Applied Catalysis B: Environmental, 2016, 181: 24-33.
［2］
ZHANG C M, ZHANG J, MA J X. Hydrogen catalytic combustion over a Pt/Ce0.6Zr0.4O2/MgAl2O4 mesoporous coating monolithic catalyst[J]. International Journal of Hydrogen Energy, 2012, 37(17): 12941-12946.
［3］
DU PREEZ S P, JONES D R, WARWICK M E A, et al. Thermally stable Pt/Ti mesh catalyst for catalytic hydrogen combustion[J]. International Journal of Hydrogen Energy, 2020, 45(33): 16851-16864.
［4］
ARZAC G M, MONTES O, FERNNDEZA A, et al. Pt-impregnated catalysts on powdery SiC and other commercial supports for the combustion of hydrogen under oxidant conditions[J]. Applied Catalysis B: Environmental, 2017, 201: 391-399.
［5］
YANG D Y, FU S Y, HUANG S S, et al. The preparation of hierarchical Pt/ZSM-5 catalysts and their performance for toluene catalytic combustion[J]. Microporous and Mesoporous Materials, doi: 10.1016/j.micromeso.2019.109802.
［6］
LUO L, WANG S, FAN C, et al. Promoting effect of alkali metal cations on the catalytic performance of Pd/H-ZSM-5 in the combustion of lean methane[J]. Applied Catalysis A: General, doi: 10.1016/j.apcata.2020.117678.
［7］
FAN C, YANG L, LUO L, et al. A highly active Pd/H-ZSM-5 catalyst in lean methane combustion prepared via a sol-gel method and treated by reduction-oxidation[J]. New Journal of Chemistry, doi: 10.1039/D0NJ00212G.
［8］
ZHANG R D, ZHANG B, SHI Z Y, et al. Catalytic behaviors of chloromethane combustion over the metal-modified ZSM-5 zeolites with diverse SiO2/Al2O3 ratios[J]. Journal of Molecular Catalysis A: Chemical, doi:10.1016/j.molcata.2014.11.019.
［9］
WU M, WANG X Y, DAI Q G, et al. Low temperature catalytic combustion of chlorobenzene over Mn-Ce-O/γ-Al2O3 mixed oxides catalyst[J]. Catalysis Today, 2010, 158(3): 336-342.
[10]
HUANG H F, JIN L L, LU H F, et al. Monolithic CrV/TiO2/cordierite catalysts prepared by in-situ precipitation and impregnation for low-temperature NH3-SCR reactions[J]. Catalysis Communications, 2013, 34: 1-4.
[11]
GIARRATANO F, ARZAC G M, GODINHO V, et al. Nanoporous Pt-based catalysts prepared by chemical dealloying of magnetron-sputtered Pt-Cu thin films for the catalytic combustion of hydrogen[J]. Applied Cata-lysis B: Environmental, 2018, 235:168-176.
[12]
HUANG S S, YANG D Y, TANG Q X, et al. Pt-loaded ellipsoidal nanozeolite as an active catalyst for toluene catalytic combustion[J]. Microporous and Mesoporous Materials, doi : 10.1016/j.micromeso.2020.110292.
[13]
ZHAO P P, CHEN J, YU H B, et al. Insights into propane combustion over MoO3 promoted Pt/ZrO2 catalysts: the generation of Pt-MoO3 interface and its promotional role on catalytic activity[J]. Journal of Catalysis, 2020, 391:80-90.
[14]
LIANG Y L, DING X M, DAI J Y, et al. Active oxygen-promoted NO catalytic on monolithic Pt-based diesel oxidation catalyst modified with Ce[J]. Catalysis Today, 2019, 327: 64-72.
JIN Q Q, XIE J L, LI F X, et al. Performance of structured cordierite catalysts with different coatings for NH3-SCR[J]. Chemical Industry and Engineering Progress, 2019, 38(3): 1411-1418. (in Chinese)
2023, Vol. 44 