Abstract:Fracture often occurs suddenly at the start-up to the impeller of high-temperature tower bottom slurry oil pump when it has been used for a period of time.To find the cause of this phenomenon,some possible factors are considered.A series of experiments were done from the macroscopic inspection which was aimed at the breakpoints to the microscopic tests,such as material composition test and hardness measurement to the impeller.Metallurgical structure test to the breakpoints were done to the model in which this phenomenon most occurred.Thermal shock theory was also applied to the failure analysis to the impeller.The analysis and test proved that there are serious casting defect in the impeller and deviation during the heat treatment and strength reduction in high temperature environment.Among them,stress derived thermal shock were the main cause for the failure of impeller.Through the improvements in the aspects of impeller structure,casting and heat treatment process,and the operating regulation during star-up,the problem of impeller fracture has been basically solved.
[1] 雷细根,易拥军,何玉杰.新型油浆泵在炼厂催化裂化装置中的应用[J].排灌机械,2005,23(2):1-3[2] Fernández,Belzunce F J.Wear and oxidation behaviour of high-chromium white cast irons[J].Materials Characterrization,2007(5):1-6[3] 中国机械工程学会铸造专业学会.铸造手册:第1卷铸铁[M].北京:机械工业出版社,2003:504-563[4] .GB/T 13298-1991.金属显微组织检验方法[S].[5] .GB/T 230.1-2004.金属洛氏硬度试验第一部分:试验方法[S].[6] .GB/T 2100-2002.一般用途耐蚀钢铸件[S].[7] Cheryl Moreland,Cliff Warne.Optimizing the working life of hydrocarbon slurry pumps[J].World Pumps,2007(9):50-54[8] 石海峡,殷为民,何玉杰.化工流程泵结构与特点[J].排灌机械,2007,25(1):65-68[9] 刘贞,王永庆,高建英.Cr26高铬白口铸铁的研究与生产[J].现代铸铁,2006(5):28-32[10] 徐秀生,王玉霞.KPY全衬里部分流型油浆泵的研制[J].农业装备与车辆工程,2007(5):51-53[11] Llewellyn R J,Yick S K,Dolmanb K F.Scouring erosion resistance of metallic materials used in slurry pump service[J].Wear,2004(256):592-599