| Resistance of manufactured sand concrete with fly ash to chloride ion attack under dry-wet cycle
|
| (Faculty of Civil Engineering and Mechanics, Jiangsu University, Zhenjiang, Jiangsu 212013, China)
|
|
|
|
|
Abstract To investigate the transportation mechanism of chloride ion in manufactured sand concrete (MSC), the chlorine salt erosion tests under dry-wet cycle were carried out under the conditions of different sand replacement rate, fly ash content and stone powder content. The mass fraction of free chloride ions and diffusion coefficient of chloride ions in concrete were obtained by the experiments. The results show that with the increasing of manufactured sand (MS) replacement, the chloride concentration at the same concrete depth and chloride diffusion coefficient of concrete is decreased with latter increasing. The concrete with 50% manufactured sand has the highest resistance performance to chloride ion penetration. With the increasing of fly ash content, the chloride penetration resistance of manufactured sand concrete is increased with latter decreasing. The manufactured sand concrete with 30% fly ash can resist the chloride penetration with the best effect. Compared with the MS without or containing 11.6% stone powder, the chloride ion erosion resistance of concrete with 5.8% stone power is the strongest. Proper amount of manufactured sand in concrete can improve the durability life of concrete in the dry-wet cycle of chloride solution.
|
|
Received: 22 December 2021
|
|
|
|
| ［1］ |
马涛. 混合砂对混凝土性能的影响及其应用[D].徐州：中国矿业大学,2020.
|
| ［2］ |
刘明辉,王雪艳,刘萱,等.硫酸钙晶须对机制砂混凝土中石粉的改性作用研究[J].土木工程学报,2021,54(5):56-64.
|
|
LIU M H, WANG X Y, LIU X, et al. Study on modification effect of calcium sulfate whiskers on stone power content of manufactured sand concrete[J]. China Civil Engineering Journal, 2021, 54(5):56-64.（in Chinese）
|
| ［3］ |
于本田,刘通,王焕,等.花岗斑岩石粉含量对混凝土性能及微观结构的影响研究[J].吉林大学学报(工学版)， DOI： 10.13229/j.cnki.jdxbgxb20200963.
|
|
YU B T, LIU T,WANG H, et al. Influence of granite porphyry stone powder content on porperties and microstructure of concrete[J].Journal of Jilin University(Engineering and Technology Edition)，DOI： 10.13229/j.cnki.jdxbgxb20200963.（in Chinese）
|
| ［4］ |
鄢佳佳, 叶仙松, 李毅超,等. 机制砂石粉含量对掺火山灰混凝土性能的影响[J]. 材料科学与工程学报, 2019, 37(5): 828-832.
|
|
YAN J J, YE X S, LI Y C, et al. Influence of stone dust content in manufactured sand on properties of concrete with volcanic ash incorpoated[J]. Journal of Materials Science and Engineering,2019,37(5):828-832.（in Chinese）
|
| ［5］ |
李北星, 尹立愿, 冯紫豪，等. 石粉含量对C60机制砂海工混凝土耐久性的影响研究[J]. 混凝土, 2017(10): 169-173.
|
|
LI B X,YIN L Y, FENG Z H, et al. Study on the effects of rock dust content on the durability of C60 ma-nufactured sand marine concrete[J]. Concrete, 2017(10):169-173.（in Chinese）
|
| ［6］ |
杨卓强,刘元珍.石粉掺量对机制砂高性能混凝土强度及耐久性能影响研究[J].混凝土, 2018（7）: 69-75.
|
|
YANG Z Q, LIU Y Z. Effect of stone powder content on strength and durability of high performance concrete with machine-made sand[J]. Concrete, 2018（7）: 69-75.（in Chinese）
|
| ［7］ |
徐志华, 邓俊双, 刘战鳌, 等. 机制砂中细粉MB值对混凝土性能影响规律的研究[J]. 武汉理工大学学报(交通科学与工程版)，2021,45（6）：1151-1157.
|
|
XU Z H, DENG J S, LIU Z A, et al. Study on the influence law of MB value of microfines in manufactured sand on concrete performances[J].Journal of Wuhan University of Technology(Transportation Science & Engineering)，2021,45（6）：1151-1157.（in Chinese）
|
| ［8］ |
李遵云,周玉娟,秦明强,等.凝灰岩机制砂海工混凝土抗氯盐侵蚀耐久性研究[J].硅酸盐通报,2015,34(4):955-959.
|
|
LI Z Y, ZHOU Y J, QIN M Q, et al. Experimental study of tuff manufactured sand on chloride resistance of marine concrete[J].Bulletin of the Chinese Ceramic Society,2015,34(4):955-959.（in Chinese）
|
| ［9］ |
胡蝶. 机制砂混凝土的工作性能、力学性能及抗氯离子侵蚀性能研究[D].广州：广州大学, 2018.
|
| ［10］ |
BOURGUIBA A, GHORBEL E, CRISTOFOL L, et al. Effects of recycled sand on the properties and durability of polymer and cement based mortars[J]. Construction and Building Materials, 2017, 153: 44-54.
|
| ［11］ |
李佩珍,谢慧才. RCT——快速氯离子检测方法及其应用[J]．混凝土, 2000(12)： 46-48.
|
|
LI P Z, XIE H C. RCT-the rapid chlorides test and its applications[J]. Concrete, 2000(12)： 46-48.（in Chinese）
|
| ［12］ |
彭建新，吴婷婷，胡守旺，等．氯盐环境下预应力混凝土梁桥氯离子扩散效应及其空间概率分析[J].中国公路学报，2016，29(4)：50-58.
|
|
PENG J X, WU T T, HU S W, et al. Effect of chlorides diffusion and its spatial probability analysis of prestressed concrete bridge under chloride environment[J]. China Journal of Highway and Transport,2016,29(4):50-58.（in Chinese）
|
| ［13］ |
金祖权,孙伟,赵铁军,等. 在不同溶液中混凝土对氯离子的固化程度[J]. 硅酸盐学报, 2009, 37(7): 1068-1072, 1078.
|
|
JIN Z Q, SUN W, ZHAO T J, et al. Chloride binding in concrete exposed to corrosive solutions[J]. Journal of the Chinese Ceramic Society, 2009, 37(7): 1068-1072, 1078.（in Chinese）
|
| ［14］ |
姚昌建.沿海码头混凝土设施受氯离子侵蚀的规律研究[D].杭州：浙江大学,2007.
|
| ［15］ |
徐鹏飞. 氯盐环境下纳米强化再生骨料混凝土梁耐久性能提升研究[D].镇江：江苏大学,2020.
|
| ［16］ |
ENGELUND S, EDVARDSEN C, MOHR L. General Guidelines for Durability Design and Redesign[M]. Brussels, Belgium: European Commission, 2000.
|
| ［17］ |
张猛.混凝土中钢筋锈蚀的氯离子临界浓度及阻锈剂影响的研究[D].哈尔滨：哈尔滨工业大学,2012.
|
|
|
|